- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.919
- 拉伸强度 [MPa]: 8.8
- 弯曲模量 [MPa]: 0.296
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D792 | ||
| Thickness | >= 25.0 microns | >= 0.984 mil | |||
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D882 | ||
| Tensile Strength, Yield | 8.80 MPa | 1280 psi | ASTM D638 | ||
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 | ||
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 | ||
| Elongation at Break | 712 % | 712 % | ASTM D638 | ||
| Flexural Modulus | 0.296 GPa | 42.9 ksi | at 1%; ASTM D790 | ||
| Secant Modulus, MD | 0.150 GPa | 21.8 ksi | at 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.175 GPa | 25.4 ksi | at 1%; ASTM D882 | ||
| Impact | 45 | 45 | J/mm; NOVA Chemicals Puncture test | ||
| Coefficient of Friction | >= 0.60 | >= 0.60 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 5.90 g/micron | 150 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 3.90 g/micron | 99.1 g/mil | ASTM D1922 | ||
| Dart Drop | 2.40 g/micron | 61.0 g/mil | F50, ASTM D1709/A | ||
| Film Tensile Strength at Break, MD | 18.0 MPa | 2610 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 16.0 MPa | 2320 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 12 % | 12 % | ASTM D1003 | ||
| Gloss | 40 % | 40 % | at 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 170 - 190 °C | 338 - 374 °F | |||
| Descriptive Properties | |||||
| Blow Up Ratio | 2:1 to 3:1 | ||||