- 熔体流动速率 [g/10min]: 0.027
- 密度 [g/cm3]: 0.917
- 拉伸强度 [MPa]: 8.8
- 弯曲强度 [MPa]: 21.0
- 弯曲模量 [MPa]: 0.660
- 热变形温度 [℃]: 59.0
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 - 0.966 g/cc | 0.0331 - 0.0349 lb/in³ | Average value: 0.951 g/cc Grade Count:157 |
| Volatiles | 0.0350 - 0.100 % | 0.0350 - 0.100 % | Average value: 0.0836 % Grade Count:10 |
| Moisture Vapor Transmission | 0.0300 - 0.260 cc-mm/m²-24hr-atm | 0.0762 - 0.660 cc-mil/100 in²-24hr-atm | Average value: 0.163 cc-mm/m²-24hr-atm Grade Count:15 |
| 0.00418 - 0.00418 cc-mm/m²-24hr-atm @Temperature 38.0 - 38.0 °C | 0.0106 - 0.0106 cc-mil/100 in²-24hr-atm @Temperature 100 - 100 °F | Average value: 0.00418 cc-mm/m²-24hr-atm Grade Count:1 | |
| Water Vapor Transmission | 0.500 - 15.5 g/m²/day | 0.0322 - 0.998 g/100 in²/day | Average value: 7.16 g/m²/day Grade Count:21 |
| 2.9488 - 10.864 g/m²/day @Temperature 37.8 - 38.0 °C | 0.18990 - 0.69964 g/100 in²/day @Temperature 100 - 100 °F | Average value: 6.01 g/m²/day Grade Count:5 | |
| Oxygen Transmission | 1.77 - 138 cc-mm/m²-24hr-atm | 4.49 - 351 cc-mil/100 in²-24hr-atm | Average value: 59.8 cc-mm/m²-24hr-atm Grade Count:5 |
| Oxygen Transmission Rate | 1490 - 5580 cc/m²/day | 95.8 - 359 cc/100 in²/day | Average value: 2400 cc/m²/day Grade Count:10 |
| Environmental Stress Crack Resistance | 2.00 - 1500 hour | 2.00 - 1500 hour | Average value: 770 hour Grade Count:7 |
| 24.0 - 24.0 hour @Temperature 50.0 - 50.0 °C | 24.0 - 24.0 hour @Temperature 122 - 122 °F | Average value: 1000 hour Grade Count:5 | |
| Thickness | 10.0 - 75.0 microns | 0.394 - 2.95 mil | Average value: 25.4 microns Grade Count:88 |
| Melt Flow | 0.0270 - 55.0 g/10 min | 0.0270 - 55.0 g/10 min | Average value: 4.95 g/10 min Grade Count:159 |
| Base Resin Melt Index | 0.0500 - 18.0 g/10 min | 0.0500 - 18.0 g/10 min | Average value: 4.90 g/10 min Grade Count:4 |
| Coating Weight | 9.00 - 28.3 g/m² | 5.63 - 17.7 lb/ream | Average value: 23.0 g/m² Grade Count:7 |
| Ash | 0.0300 - 0.0600 % | 0.0300 - 0.0600 % | Average value: 0.0544 % Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 28.0 - 69.0 | 28.0 - 69.0 | Average value: 60.5 Grade Count:21 |
| Tensile Strength, Ultimate | 21.0 - 40.0 MPa | 3050 - 5800 psi | Average value: 31.6 MPa Grade Count:16 |
| Film Tensile Strength at Yield, MD | 11.6 - 51.7 MPa | 1680 - 7500 psi | Average value: 30.7 MPa Grade Count:69 |
| Film Tensile Strength at Yield, TD | 12.1 - 228 MPa | 1750 - 33000 psi | Average value: 31.3 MPa Grade Count:72 |
| Tensile Strength, Yield | 8.80 - 35.0 MPa | 1280 - 5080 psi | Average value: 18.5 MPa Grade Count:28 |
| Film Elongation at Break, MD | 160 - 1350 % | 160 - 1350 % | Average value: 511 % Grade Count:117 |
| Film Elongation at Break, TD | 3.00 - 1010 % | 3.00 - 1010 % | Average value: 565 % Grade Count:115 |
| Elongation at Break | 400 - 1700 % | 400 - 1700 % | Average value: 689 % Grade Count:33 |
| Elongation at Yield | 8.00 - 850 % | 8.00 - 850 % | Average value: 219 % Grade Count:4 |
| Modulus of Elasticity | 0.0200 - 1.10 GPa | 2.90 - 160 ksi | Average value: 0.678 GPa Grade Count:9 |
| Flexural Modulus | 0.660 - 1.47 GPa | 95.7 - 213 ksi | Average value: 1.05 GPa Grade Count:11 |
| Secant Modulus, MD | 0.0300 - 1.40 GPa | 4.35 - 203 ksi | Average value: 0.841 GPa Grade Count:85 |
| Secant Modulus, TD | 0.0500 - 1.70 GPa | 7.25 - 247 ksi | Average value: 1.00 GPa Grade Count:85 |
| Dart Drop, Total Energy | 2.44 - 2.71 J | 1.80 - 2.00 ft-lb | Average value: 2.53 J Grade Count:3 |
| Puncture Energy | 0.722 - 2.14 J | 0.533 - 1.58 ft-lb | Average value: 1.36 J Grade Count:7 |
| Coefficient of Friction | 0.240 - 0.400 | 0.240 - 0.400 | Average value: 0.286 Grade Count:9 |
| Coefficient of Friction, Static | 0.100 - 0.250 | 0.100 - 0.250 | Average value: 0.175 Grade Count:6 |
| Tear Strength Test | 9.80 - 27.4 | 9.80 - 27.4 | Average value: 15.2 Grade Count:15 |
| Elmendorf Tear Strength MD | 1.40 - 70.0 g | 1.40 - 70.0 g | Average value: 20.9 g Grade Count:67 |
| Elmendorf Tear Strength TD | 10.0 - 1800 g | 10.0 - 1800 g | Average value: 291 g Grade Count:66 |
| Elmendorf Tear Strength, MD | 0.200 - 70.0 g/micron | 5.08 - 1780 g/mil | Average value: 1.77 g/micron Grade Count:69 |
| Elmendorf Tear Strength, TD | 0.400 - 150 g/micron | 10.2 - 3810 g/mil | Average value: 11.9 g/micron Grade Count:70 |
| Dart Drop | 0.890 - 30.0 g/micron | 22.6 - 762 g/mil | Average value: 8.04 g/micron Grade Count:56 |
| Dart drop Test | 20.0 - 1000 g | 0.0441 - 2.20 lb | Average value: 217 g Grade Count:68 |
| Film Tensile Strength at Break, MD | 24.1 - 141 MPa | 3500 - 20500 psi | Average value: 55.6 MPa Grade Count:114 |
| Film Tensile Strength at Break, TD | 17.9 - 251 MPa | 2600 - 36400 psi | Average value: 49.2 MPa Grade Count:114 |
| Heat Seal Strength Initiation Temperature | 125 °C | 257 °F | Average value: 125 °C Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.33 | 2.33 | Average value: 2.33 Grade Count:3 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | Average value: 20.0 kV/mm Grade Count:3 |
| Dissipation Factor | 0.000100 | 0.000100 | Average value: 0.000100 Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 72.0 - 135 °C | 162 - 275 °F | Average value: 127 °C Grade Count:49 |
| Deflection Temperature at 0.46 MPa (66 psi) | 59.0 - 64.0 °C | 138 - 147 °F | Average value: 62.3 °C Grade Count:3 |
| Vicat Softening Point | 41.0 - 243 °C | 106 - 469 °F | Average value: 119 °C Grade Count:51 |
| Softening Point | 73.0 - 75.0 °C | 163 - 167 °F | Average value: 74.2 °C Grade Count:5 |
| Brittleness Temperature | -80.0 - -59.0 °C | -112 - -74.2 °F | Average value: -70.8 °C Grade Count:21 |
| Shrinkage | 1.70 - 5.00 % | 1.70 - 5.00 % | Average value: 2.96 % Grade Count:5 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.00 - 81.0 % | 4.00 - 81.0 % | Average value: 29.3 % Grade Count:27 |
| Gloss | 5.00 - 127 % | 5.00 - 127 % | Average value: 62.0 % Grade Count:26 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 232 °C | 68.0 - 450 °F | Average value: 180 °C Grade Count:11 |
| Melt Temperature | 124 - 280 °C | 255 - 536 °F | Average value: 207 °C Grade Count:58 |
| Die Opening | 0.0760 - 0.280 cm | 0.0299 - 0.110 in | Average value: 0.164 cm Grade Count:8 |
| Blow-up Ratio (BUR) | 1.50 - 5.00 | 1.50 - 5.00 | Average value: 3.58 Grade Count:29 |