- 熔体流动速率 [g/10min]: 0.029
- 密度 [g/cm3]: 0.91
- 缺口冲击强度: 0.785
- 拉伸强度 [MPa]: 16.5
- 弯曲强度 [MPa]: 18.0
- 弯曲模量 [MPa]: 0.621
- 热变形温度 [℃]: 57.0
- 脆化温度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 - 0.970 g/cc | 0.0329 - 0.0350 lb/in³ | Average value: 0.951 g/cc Grade Count:135 |
| Volatiles | 0.0350 % | 0.0350 % | Average value: 0.0350 % Grade Count:3 |
| Viscosity | 270000 - 2.10e+6 cP @Temperature 190 - 190 °C | 270000 - 2.10e+6 cP @Temperature 374 - 374 °F | Average value: 1.26e+6 cP Grade Count:7 |
| 270000 - 2.10e+6 cP @Shear Rate 100 - 1000 1/s | 270000 - 2.10e+6 cP @Shear Rate 100 - 1000 1/s | Average value: 1.26e+6 cP Grade Count:7 | |
| Environmental Stress Crack Resistance | 10.0 - 10000 hour | 10.0 - 10000 hour | Average value: 3220 hour Grade Count:44 |
| 15.5 - 15.5 hour @Temperature 50.0 - 100 °C | 15.5 - 15.5 hour @Temperature 122 - 212 °F | Average value: 1290 hour Grade Count:17 | |
| >= 5.00 hour @Temperature 80.0 - 80.0 °C | >= 5.00 hour @Temperature 176 - 176 °F | Average value: 1290 hour Grade Count:2 | |
| >= 5.00 hour @Pressure 0.920 - 0.920 MPa | >= 5.00 hour @Pressure 133 - 133 psi | Average value: 1290 hour Grade Count:2 | |
| 530 - 530 hour @Temperature 50.0 - 100 °C | 530 - 530 hour @Temperature 122 - 212 °F | Average value: 1290 hour Grade Count:8 | |
| 530 - 530 hour @Thickness 1.90 - 2.00 mm | 530 - 530 hour @Thickness 0.0748 - 0.0787 in | Average value: 1290 hour Grade Count:8 | |
| Oxidative Induction Time (OIT) | 10.0 - 118 min | 10.0 - 118 min | Average value: 27.0 min Grade Count:25 |
| >= 20.0 min @Temperature 200 - 210 °C | >= 20.0 min @Temperature 392 - 410 °F | Average value: 49.3 min Grade Count:15 | |
| Carbon Black Loading | 2.00 - 2.50 % | 2.00 - 2.50 % | Average value: 2.24 % Grade Count:21 |
| Melt Flow | 0.0290 - 47.0 g/10 min | 0.0290 - 47.0 g/10 min | Average value: 4.98 g/10 min Grade Count:143 |
| Base Resin Melt Index | 0.400 - 0.400 g/10 min @Temperature 190 - 190 °C | 0.400 - 0.400 g/10 min @Temperature 374 - 374 °F | Average value: 0.400 g/10 min Grade Count:1 |
| 0.400 - 0.400 g/10 min @Load 5.00 - 5.00 kg | 0.400 - 0.400 g/10 min @Load 11.0 - 11.0 lb | Average value: 0.400 g/10 min Grade Count:1 | |
| Mechanical Properties | Metric | English | Comments |
| PENT | 30.0 - 10000 hour | 30.0 - 10000 hour | Average value: 2440 hour Grade Count:16 |
| >= 1500 hour @Temperature 80.0 - 80.0 °C | >= 1500 hour @Temperature 176 - 176 °F | Average value: 1750 hour Grade Count:2 | |
| Hardness, Shore D | 57.0 - 68.0 | 57.0 - 68.0 | Average value: 63.5 Grade Count:66 |
| Tensile Strength, Ultimate | 18.0 - 38.0 MPa | 2610 - 5510 psi | Average value: 32.4 MPa Grade Count:60 |
| Tensile Strength, Yield | 16.5 - 31.0 MPa | 2390 - 4500 psi | Average value: 23.4 MPa Grade Count:114 |
| Elongation at Break | 195 - 1000 % | 195 - 1000 % | Average value: 705 % Grade Count:101 |
| Elongation at Yield | 7.30 - 600 % | 7.30 - 600 % | Average value: 93.6 % Grade Count:36 |
| Modulus of Elasticity | 0.700 - 1.34 GPa | 102 - 195 ksi | Average value: 0.961 GPa Grade Count:20 |
| Flexural Modulus | 0.621 - 1.65 GPa | 90.0 - 240 ksi | Average value: 0.991 GPa Grade Count:88 |
| Secant Modulus | 0.785 - 1.25 GPa | 114 - 181 ksi | Average value: 0.999 GPa Grade Count:6 |
| Izod Impact, Notched | 0.785 - 5.87 J/cm | 1.47 - 11.0 ft-lb/in | Average value: 2.98 J/cm Grade Count:40 |
| 0.490332 - 3.43233 J/cm @Temperature -20.0 - 0.000 °C | 0.918594 - 6.43016 ft-lb/in @Temperature -4.00 - 32.0 °F | Average value: 1.91 J/cm Grade Count:9 | |
| Izod Impact, Notched (ISO) | 10.0 - 20.0 kJ/m² | 4.76 - 9.52 ft-lb/in² | Average value: 16.6 kJ/m² Grade Count:7 |
| Charpy Impact, Notched | 1.00 - 1000 J/cm² | 4.76 - 4760 ft-lb/in² | Average value: 2.00 J/cm² Grade Count:7 |
| 0.800 - 1.60 J/cm² @Temperature -30.0 - 0.000 °C | 3.81 - 7.61 ft-lb/in² @Temperature -22.0 - 32.0 °F | Average value: 1.23 J/cm² Grade Count:3 | |
| Hydrostatic Design Basis | 5.50 - 11.0 MPa | 798 - 1600 psi | Average value: 10.1 MPa Grade Count:20 |
| 6.89476 - 6.90 MPa @Temperature 60.0 - 60.0 °C | 1000.00 - 1000 psi @Temperature 140 - 140 °F | Average value: 6.90 MPa Grade Count:8 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 - 1.00e+17 ohm-cm | 1.00e+16 - 1.00e+17 ohm-cm | Average value: 2.50e+16 ohm-cm Grade Count:6 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | Average value: 1.00e+16 ohm Grade Count:4 |
| Dielectric Constant | 2.35 - 2.45 | 2.35 - 2.45 | Average value: 2.38 Grade Count:6 |
| Dielectric Strength | 16.0 - 27.6 kV/mm | 406 - 700 kV/in | Average value: 18.4 kV/mm Grade Count:6 |
| Dissipation Factor | 0.0000500 - 0.0200 | 0.0000500 - 0.0200 | Average value: 0.00586 Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| Oxidation Induction Time | >= 20.0 min @Temperature 210 - 210 °C | >= 20.0 min @Temperature 410 - 410 °F | Average value: 20.0 min Grade Count:2 |
| Heat of Fusion | 152 - 175 J/g | 65.4 - 75.3 BTU/lb | Average value: 165 J/g Grade Count:5 |
| CTE, linear | 120 - 216 µm/m-°C | 66.7 - 120 µin/in-°F | Average value: 161 µm/m-°C Grade Count:12 |
| 90.0 - 500 µm/m-°C @Temperature -20.0 - 100 °C | 50.0 - 278 µin/in-°F @Temperature -4.00 - 212 °F | Average value: 295 µm/m-°C Grade Count:1 | |
| Specific Heat Capacity | 2.00 - 2.10 J/g-°C | 0.478 - 0.502 BTU/lb-°F | Average value: 2.01 J/g-°C Grade Count:9 |
| 2.60 - 2.60 J/g-°C @Temperature 150 - 150 °C | 0.621 - 0.621 BTU/lb-°F @Temperature 302 - 302 °F | Average value: 2.60 J/g-°C Grade Count:8 | |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | Average value: 0.400 W/m-K Grade Count:7 |
| 0.200 - 0.200 W/m-K @Temperature 150 - 150 °C | 1.39 - 1.39 BTU-in/hr-ft²-°F @Temperature 302 - 302 °F | Average value: 0.200 W/m-K Grade Count:8 | |
| Melting Point | 56.7 - 138 °C | 134 - 280 °F | Average value: 125 °C Grade Count:31 |
| Maximum Service Temperature, Air | 200 - 264 °C | 392 - 507 °F | Average value: 213 °C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 57.0 - 99.0 °C | 135 - 210 °F | Average value: 73.1 °C Grade Count:15 |
| Vicat Softening Point | 67.0 - 132 °C | 153 - 270 °F | Average value: 118 °C Grade Count:58 |
| Brittleness Temperature | -118 - -59.0 °C | -180 - -74.2 °F | Average value: -81.4 °C Grade Count:56 |
| DSC Induction Temperature | 250 °C | 482 °F | Average value: 250 °C Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Die Temperature | 200 - 210 °C | 392 - 410 °F | Average value: 205 °C Grade Count:7 |
| Melt Temperature | 136 - 260 °C | 277 - 500 °F | Average value: 206 °C Grade Count:21 |
| Head Temperature | 200 - 210 °C | 392 - 410 °F | Average value: 205 °C Grade Count:6 |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 2.00 - 2.50 % | 2.00 - 2.50 % | Average value: 2.30 % Grade Count:3 |