- 熔体流动速率 [g/10min]: 0.1
- 密度 [g/cm3]: 0.92
- 缺口冲击强度: 4.0
- 拉伸强度 [MPa]: 14.0
- 断裂伸长率 [%]: 11.0
- 弯曲强度 [MPa]: 0.13
- 弯曲模量 [MPa]: 0.400
- 热变形温度 [℃]: 65.0
- 脆化温度 [℃]: -91.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 - 1.45 g/cc | 0.0332 - 0.0524 lb/in³ | Average value: 0.946 g/cc Grade Count:144 |
| Water Absorption | 0.000 - 0.200 % | 0.000 - 0.200 % | Average value: 0.0498 % Grade Count:55 |
| Moisture Absorption at Equilibrium | 0.000 - 0.200 % | 0.000 - 0.200 % | Average value: 0.0624 % Grade Count:38 |
| Water Absorption at Saturation | 0.000 - 0.200 % | 0.000 - 0.200 % | Average value: 0.0480 % Grade Count:59 |
| Particle Size | 10.0 - 710 µm | 10.0 - 710 µm | Average value: 176 µm Grade Count:16 |
| Viscosity Measurement | 4.70 - 3450 | 4.70 - 3450 | Average value: 1120 Grade Count:16 |
| Viscosity Test | 470 - 4300 cm³/g | 470 - 4300 cm³/g | Average value: 2820 cm³/g Grade Count:8 |
| Environmental Stress Crack Resistance | 300 - 600 hour | 300 - 600 hour | Average value: 500 hour Grade Count:3 |
| >= 600 hour @Temperature 50.0 - 50.0 °C | >= 600 hour @Temperature 122 - 122 °F | Average value: 700 hour Grade Count:4 | |
| Oxidative Induction Time (OIT) | >= 50.0 min @Temperature 210 - 210 °C | >= 50.0 min @Temperature 410 - 410 °F | Average value: 50.0 min Grade Count:1 |
| Molecular Weight | 300000 - 9.20e+6 g/mol | 300000 - 9.20e+6 g/mol | Average value: 4.97e+6 g/mol Grade Count:39 |
| Melt Flow | 0.100 - 12.0 g/10 min | 0.100 - 12.0 g/10 min | Average value: 3.08 g/10 min Grade Count:18 |
| Outgassing - Total Mass Loss | 0.140 % | 0.140 % | Average value: 0.140 % Grade Count:16 |
| Surface Tension | 55.0 dynes/cm | 55.0 dynes/cm | Average value: 55.0 dynes/cm Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 54.0 - 120 | 54.0 - 120 | Average value: 63.7 Grade Count:125 |
| Ball Indentation Hardness | 24.0 - 57.0 MPa | 3480 - 8270 psi | Average value: 36.9 MPa Grade Count:48 |
| Tensile Strength, Ultimate | 0.130 - 85.5 MPa | 18.9 - 12400 psi | Average value: 27.3 MPa Grade Count:89 |
| 35.0 - 35.0 MPa @Temperature 32.0 - 32.0 °C | 5080 - 5080 psi @Temperature 89.6 - 89.6 °F | Average value: 35.0 MPa Grade Count:1 | |
| Tensile Strength, Yield | 14.0 - 40.0 MPa | 2030 - 5800 psi | Average value: 20.0 MPa Grade Count:76 |
| Elongation at Break | 25.0 - 800 % | 25.0 - 800 % | Average value: 213 % Grade Count:126 |
| Elongation at Yield | 0.200 - 350 % | 0.200 - 350 % | Average value: 26.7 % Grade Count:29 |
| Creep Strength | 3.20 - 13.0 MPa | 464 - 1890 psi | Average value: 9.74 MPa Grade Count:29 |
| Modulus of Elasticity | 0.300 - 1.30 GPa | 43.5 - 189 ksi | Average value: 0.724 GPa Grade Count:72 |
| Flexural Yield Strength | 11.0 - 40.0 MPa | 1600 - 5800 psi | Average value: 21.0 MPa Grade Count:39 |
| Flexural Modulus | 0.400 - 1.45 GPa | 58.0 - 210 ksi | Average value: 0.806 GPa Grade Count:33 |
| Compressive Yield Strength | 4.00 - 82.7 MPa | 580 - 12000 psi | Average value: 14.4 MPa Grade Count:53 |
| Compressive Modulus | 0.290 - 0.689 GPa | 42.0 - 100 ksi | Average value: 0.559 GPa Grade Count:22 |
| Shear Strength | 33.1 MPa | 4800 psi | Average value: 33.1 MPa Grade Count:8 |
| Izod Impact, Notched | 4.00 - 5340 J/cm | 7.50 - 10000 ft-lb/in | Average value: 7.54 J/cm Grade Count:27 |
| Izod Impact, Unnotched | 0.641 J/cm - NB | 1.20 ft-lb/in - NB | Average value: 0.641 J/cm Grade Count:6 |
| 5338.47 - 5338.47 J/cm @Temperature -40.0 - -40.0 °C | 10001.1 - 10001.1 ft-lb/in @Temperature -40.0 - -40.0 °F | Grade Count:1 | |
| Izod Impact, Notched (ISO) | 12.0 - 100000 kJ/m² | 5.71 - 47600 ft-lb/in² | Average value: 110 kJ/m² Grade Count:14 |
| Charpy Impact Unnotched | 1.00 J/cm² - NB | 4.76 ft-lb/in² - NB | Average value: 3.77 J/cm² Grade Count:30 |
| Charpy Impact, Notched | 2.50 J/cm² - NB | 11.9 ft-lb/in² - NB | Average value: 11.7 J/cm² Grade Count:57 |
| 3.00 - 3.00 J/cm² @Temperature -20.0 - -20.0 °C | 14.3 - 14.3 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 3.00 J/cm² Grade Count:1 | |
| Coefficient of Friction | 0.0200 - 0.350 | 0.0200 - 0.350 | Average value: 0.144 Grade Count:111 |
| 0.180 - 0.180 @Temperature 60.0 - 60.0 °C | 0.180 - 0.180 @Temperature 140 - 140 °F | Average value: 0.180 Grade Count:1 | |
| Coefficient of Friction, Static | 0.0800 - 0.200 | 0.0800 - 0.200 | Average value: 0.148 Grade Count:40 |
| Tensile Creep Modulus, 1 hour | 370 - 550 MPa | 53700 - 79800 psi | Average value: 446 MPa Grade Count:7 |
| Tensile Creep Modulus, 1000 hours | 180 - 270 MPa | 26100 - 39200 psi | Average value: 229 MPa Grade Count:7 |
| K Factor (Wear Factor) | 1.00e-9 - 110 | 1.00e-9 - 110 | Average value: 82.9 Grade Count:8 |
| Limiting Pressure Velocity | 0.0500 - 0.140 MPa-m/sec | 1430 - 4000 psi-ft/min | Average value: 0.0824 MPa-m/sec Grade Count:36 |
| Compression Set | 1.10 - 1.60 % @Temperature 80.0 - 80.0 °C | 1.10 - 1.60 % @Temperature 176 - 176 °F | Average value: 1.35 % Grade Count:1 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 100 - 1.00e+18 ohm-cm | 100 - 1.00e+18 ohm-cm | Average value: 1.41e+16 ohm-cm Grade Count:81 |
| Surface Resistance | 100 - 1.00e+15 ohm | 100 - 1.00e+15 ohm | Average value: 9.85e+13 ohm Grade Count:82 |
| Dielectric Constant | 2.10 - 3.00 | 2.10 - 3.00 | Average value: 2.54 Grade Count:30 |
| Dielectric Strength | 35.4 - 900 kV/mm | 899 - 22900 kV/in | Average value: 105 kV/mm Grade Count:48 |
| Dissipation Factor | 0.000190 - 0.00100 | 0.000190 - 0.00100 | Average value: 0.000578 Grade Count:22 |
| Dielectric Loss Index | 0.000100 - 0.00100 | 0.000100 - 0.00100 | Average value: 0.000317 Grade Count:8 |
| Arc Resistance | 180 - 240 sec | 180 - 240 sec | Average value: 210 sec Grade Count:3 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:12 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 - 200 µm/m-°C | 11.1 - 111 µin/in-°F | Average value: 192 µm/m-°C Grade Count:109 |
| Specific Heat Capacity | 1.84 - 2.30 J/g-°C | 0.440 - 0.550 BTU/lb-°F | Average value: 1.87 J/g-°C Grade Count:8 |
| Thermal Conductivity | 0.330 - 0.420 W/m-K | 2.29 - 2.91 BTU-in/hr-ft²-°F | Average value: 0.402 W/m-K Grade Count:58 |
| Melting Point | 127 - 255 °C | 260 - 491 °F | Average value: 136 °C Grade Count:96 |
| Maximum Service Temperature, Air | 70.0 - 135 °C | 158 - 275 °F | Average value: 85.4 °C Grade Count:102 |
| Deflection Temperature at 0.46 MPa (66 psi) | 65.0 - 95.0 °C | 149 - 203 °F | Average value: 71.2 °C Grade Count:14 |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 - 47.0 °C | 108 - 117 °F | Average value: 44.3 °C Grade Count:50 |
| Vicat Softening Point | 76.0 - 270 °C | 169 - 518 °F | Average value: 92.7 °C Grade Count:16 |
| Minimum Service Temperature, Air | -269 - -50.0 °C | -452 - -58.0 °F | Average value: -176 °C Grade Count:30 |
| Brittleness Temperature | -91.0 - 103 °C | -132 - 217 °F | Average value: -57.9 °C Grade Count:7 |
| Glass Transition Temp, Tg | -120 °C | -184 °F | Average value: -120 °C Grade Count:13 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:69 |
| Oxygen Index | 20.0 - 28.0 % | 20.0 - 28.0 % | Average value: 20.5 % Grade Count:16 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 154 - 268 °C | 309 - 514 °F | Average value: 209 °C Grade Count:4 |
| Melt Temperature | 136 - 220 °C | 277 - 428 °F | Average value: 169 °C Grade Count:3 |