- 密度 [g/cm3]: 0.93
- 吸水率 [%]: 0.01
- 拉伸强度 [MPa]: 19.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.010 % | 0.010 % | immersion | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 60 | 60 | after 15 sec.; ISO 868 | ||
| 62 | 62 | after 3 sec.; ISO 868 | |||
| Ball Indentation Hardness | 36.0 MPa | 5220 psi | ISO 2039-1 | ||
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ISO 527 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527 | ||
| Elongation at Yield | 15 % | 15 % | ISO 527 | ||
| Tensile Modulus | 0.750 GPa | 109 ksi | ISO 527 | ||
| Compressive Yield Strength | 4.50 MPa | 653 psi | at 1% nominal strain; ISO 604 | ||
| 8.00 MPa | 1160 psi | at 2% nominal strain; ISO 604 | |||
| 14.0 MPa | 2030 psi | at 5% nominal strain; ISO 604 | |||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 11.0 J/cm² | 52.4 ft-lb/in² | Partial Break; ISO 179/1eA | ||
| Abrasion | 100 | 100 | Relative loss per DSM internal test (CESTILENE HD 1000 = 100) | ||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 93 | ||
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 93 | ||
| Dielectric Constant | 2.1 @Frequency 100 Hz | 2.1 @Frequency 100 Hz | IEC 250 | ||
| 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | IEC 250 | |||
| Dielectric Strength | <= 45.0 kV/mm | <= 1140 kV/in | IEC 243 | ||
| Dissipation Factor | 0.00040 @Frequency 100 Hz | 0.00040 @Frequency 100 Hz | IEC 250 | ||
| 0.0010 @Frequency 1e+6 Hz | 0.0010 @Frequency 1e+6 Hz | IEC 250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 175 - 225 µm/m-°C @Temperature 20.0 °C | 97.2 - 125 µin/in-°F @Temperature 68.0 °F | |||
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | |||
| Melting Point | 130 - 135 °C | 266 - 275 °F | ISO 3146; DSC, 10°C/min | ||
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | 20,000 hours continuous | ||
| 120 °C | 248 °F | for short periods | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75 method A | ||
| Vicat Softening Point | 80.0 °C | 176 °F | ISO 306 | ||
| Minimum Service Temperature, Air | -200 °C | -328 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Oxygen Index | <= 20 % | <= 20 % | ISO 4589 | ||
| Descriptive Properties | |||||
| Color | natural (white) / black / green | ||||