- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.954
- 拉伸强度 [MPa]: 22.0
- 热变形温度 [℃]: 65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | ISO 1183 |
| ESCR 10% Igepal® | >= 40 hour | >= 40 hour | ASTM D1693 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | ISO 868 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 10 % | 10 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 0.850 GPa | 123 ksi | At 1 mm/min; ISO 527-2 |
| Tensile Impact Strength | 80.0 kJ/m² | 38.1 ft-lb/in² | ISO 8256/A1 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 65.0 °C | 149 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 190 - 250 °C | 374 - 482 °F | |
| Mold Temperature | 10.0 - 40.0 °C | 50.0 - 104 °F | |