- 熔体流动速率 [g/10min]: 0.55
- 密度 [g/cm3]: 0.959
- 拉伸强度 [MPa]: 24.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.959 g/cc | 0.0346 lb/in³ | ISO 1872-2/ISO 1183 | ||
| Environmental Stress Crack Resistance | 1.0 hour @Pressure 0.920 MPa, Temperature 80.0 °C | 1.0 hour @Pressure 133 psi, Temperature 176 °F | ISO 13479 | ||
| Oxidative Induction Time (OIT) | >= 20 min @Temperature 200 °C | >= 20 min @Temperature 392 °F | EN 728 | ||
| Carbon Black Loading | 2.0 % | 2.0 % | ASTM D1603 | ||
| Melt Flow | 0.55 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.55 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527-2 | ||
| Elongation at Break | >= 600 % | >= 600 % | ISO 527-2 | ||
| Tensile Modulus | 1.10 GPa | 160 ksi | ISO 527-3 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 190 - 260 °C | 374 - 500 °F | |||
| Descriptive Properties | |||||
| Carbon Black Dispersion | < 3 | ISO 18553 | |||