- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 0.948
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 1.05
- 热变形温度 [℃]: 76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ISO 1183 |
| Environmental Stress Crack Resistance | 300 hour | 300 hour | Antarox 10%, F50; ASTM D1693-A |
| Melt Flow | 7.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 7.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ISO 868 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 10 % | 10 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.00 GPa | 145 ksi | 1mm/min; ISO 527-2 |
| Flexural Modulus | 1.05 GPa | 152 ksi | 1mm/min; ISO 178 |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -20.0 °C | 9.52 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA |
| 2.50 J/cm² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C | 169 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 190 - 220 °C | 374 - 428 °F | |
| Die Temperature | 180 - 220 °C | 356 - 428 °F | |
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |