- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.956
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.956 g/cc | 0.0345 lb/in³ | ISO 1183 |
| Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.30 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 |
| 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 9.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 250 % | 250 % | ISO 527-3 |
| Film Elongation at Break, TD | 300 % | 300 % | ISO 527-3 |
| Tensile Modulus | 1.00 GPa | 145 ksi | MD; ASTM D882-A |
| 1.10 GPa | 160 ksi | TD; ASTM D882-A | |
| Puncture Energy | 1.50 J | 1.11 ft-lb | 45N; ASTM D5748 |
| Elmendorf Tear Strength MD | 20.387 g | 20.387 g | ISO 6383/2 |
| Elmendorf Tear Strength TD | 30.58 g | 30.58 g | ISO 6383/2 |
| Dart drop Test | 350 g | 0.772 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 55.0 MPa | 7980 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 133 °C | 271 °F | ISO 11357-3 |
| Vicat Softening Point | 127 °C | 261 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 230 °C | 410 - 446 °F | |