- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.963
- 拉伸强度 [MPa]: 32.0
- 弯曲模量 [MPa]: 1.60
- 热变形温度 [℃]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.963 g/cc | 0.0348 lb/in³ | ISO 1183 |
| Environmental Stress Crack Resistance | 10 hour | 10 hour | Antarox 10%, F50; ASTM D1693-A |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 2.2 g/10 min @Load 5.00 kg, Temperature 190 °C | 2.2 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |
| 44 g/10 min @Load 21.6 kg, Temperature 190 °C | 44 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 68 | 68 | ISO 868 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 8.0 % | 8.0 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.50 GPa | 218 ksi | 1mm/min; ISO 527-2 |
| Flexural Modulus | 1.60 GPa | 232 ksi | 1mm/min; ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C | 192 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 180 - 220 °C | 356 - 428 °F | |
| Die Temperature | 180 - 220 °C | 356 - 428 °F | |
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |