- 熔体流动速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.957
- 拉伸强度 [MPa]: 29.0
- 弯曲模量 [MPa]: 1.35
- 热变形温度 [℃]: 78.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.957 g/cc | 0.0346 lb/in³ | ISO 1183 |
| Environmental Stress Crack Resistance | 40 hour | 40 hour | Antarox 10%, F50; ASTM D1693-A |
| Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.20 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C | 1.0 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |
| 23 g/10 min @Load 21.6 kg, Temperature 190 °C | 23 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ISO 868 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 8.0 % | 8.0 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.25 GPa | 181 ksi | 1mm/min; ISO 527-2 |
| Flexural Modulus | 1.35 GPa | 196 ksi | 1mm/min; ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 190 - 220 °C | 374 - 428 °F | |
| Die Temperature | 180 - 220 °C | 356 - 428 °F | |
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |