- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.954
- 缺口冲击强度: 27.3
- 拉伸强度 [MPa]: 27.6
- 弯曲模量 [MPa]: 1.40
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | ASTM D-792 | ||
| ESCR 100% Igepal® | 500 hour | 500 hour | >500; ASTM D-1693 | ||
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | HLMI; ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D-638 | ||
| Elongation at Break | 820 % | 820 % | ASTM D-638 | ||
| Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D-790 | ||
| Izod Impact, Notched (ISO) | 27.3 kJ/m² | 13.0 ft-lb/in² | ASTM D-256 | ||
| Descriptive Properties | |||||
| process | Blow Molding | ||||
| region | Europe/Turkey | ||||
| International | |||||
| Mexico | |||||
| US & Canada | |||||