- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 1.145
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D1505 | ||
| ESCR 100% Igepal® | 24 hour @Thickness 3.00 mm, Temperature 23.0 °C | 24 hour @Thickness 0.118 in, Temperature 73.4 °F | compression molded plaques; ASTM D1693B | ||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 64 | 64 | ASTM D2240 | ||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D638 | ||
| Film Tensile Strength at Yield, MD | 26.0 MPa | 3770 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 30.0 MPa | 4350 psi | ASTM D882 | ||
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 | ||
| Film Elongation at Break, MD | 1300 % | 1300 % | ASTM D882 | ||
| Film Elongation at Break, TD | >= 1700 % | >= 1700 % | ASTM D882 | ||
| Flexural Modulus | 1.145 GPa | 166.1 ksi | ASTM D790 | ||
| Elmendorf Tear Strength, MD | 0.700 g/micron | 17.8 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 1.90 g/micron | 48.3 g/mil | ASTM D1922 | ||
| Film Tensile Strength at Break, MD | 49.0 MPa | 7110 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Minimum Recommended Thickness | 15 µm | ||||
| Puncture Strength | 26 J/mm | Braskem® Method | |||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.