- 密度 [g/cm3]: 0.955
- 拉伸强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 1.37
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D-1505 |
| ESCR 100% Igepal® | 30 hour | 30 hour | Condition B, F50; ASTM D-1693 |
| Melt Index of Compound | 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.35 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 2 in/min, Type IV bar; ASTM D-638 |
| Elongation at Break | 500 % | 500 % | 2 in/min, Type IV bar; ASTM D-638 |
| Flexural Modulus | 1.37 GPa | 199 ksi | Tangent - 16:1 span:depth, 0.5 in/min; ASTM D-790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A, Type I specimen; ASTM D-746 |