- 密度 [g/cm3]: 0.945
- 拉伸强度 [MPa]: 22.0
- 弯曲模量 [MPa]: 1.10
- 脆化温度 [℃]: -79.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 2000 hour @Temperature 50.0 °C | >= 2000 hour @Temperature 122 °F | Condition A and Condition B; ASTM D 1693 |
| High Load Melt Index | 5.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 5.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 Type IV |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 Type IV |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 127.22 °C | 261.00 °F | ASTM D1525 |
| Brittleness Temperature | -79.0 °C | -110 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 221 °C | 379 - 430 °F | Blow Molding |