- 密度 [g/cm3]: 0.96
- 弯曲强度 [MPa]: 31.7
- 弯曲模量 [MPa]: 1.55
- 热变形温度 [℃]: 82.2
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D1505 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength, Ultimate | 31.7 MPa | 4600 psi | ASTM D638 |
| Elongation at Yield | >= 400 % | >= 400 % | ASTM D638 |
| Flexural Modulus | 1.55 GPa | 225 ksi | ASTM D790 |
| Tensile Impact | 64.1 J/cm | 120 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 |