- 熔体流动速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.952
- 拉伸强度 [MPa]: 26.2
- 弯曲模量 [MPa]: 1.28
- 热变形温度 [℃]: 72.0
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 - 0.955 g/cc | 0.0344 - 0.0345 lb/in³ | ASTM D1505 |
| Linear Mold Shrinkage | 0.015 - 0.050 cm/cm | 0.015 - 0.050 in/in | |
| Melt Flow | 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.25 g/10 min @Load 4.76 lb, Temperature 374 °F | Procedure A Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | 2 in per min; ASTM D638 |
| Elongation at Break | 1200 % | 1200 % | |
| Flexural Modulus | 1.28 GPa | 185 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Tensile Impact Strength | 210 kJ/m² | 100 ft-lb/in² | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 |