- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.948
- 弯曲模量 [MPa]: 0.586
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ASTM D1505 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F | Procedure A Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 22.1 MPa | 3200 psi | ASTM D638 |
| Elongation at Break | 19 % | 19 % | ASTM D638 |
| Flexural Modulus | 0.586 GPa | 85.0 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -70.0 °C | -94.0 °F | |