- 熔体流动速率 [g/10min]: 10.0
- 密度 [g/cm3]: 0.962
- 拉伸强度 [MPa]: 23.4
- 弯曲强度 [MPa]: 12.4
- 弯曲模量 [MPa]: 1.08
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | |
| Viscosity | 80000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 80000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 180000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 180000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 260000 cP @Shear Rate 300 1/s, Temperature 190 °C | 260000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 10 g/10 min @Load 2.16 kg | 10 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 12.4 MPa | 1800 psi | |
| Tensile Strength, Yield | 23.4 MPa | 3390 psi | |
| Elongation at Break | 1000 % | 1000 % | |
| Modulus of Elasticity | 0.745 GPa | 108 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 1.08 GPa | 157 ksi | |
| Izod Impact Resistance | 9.61 J/cm² | 45.7 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 128 °C | 262 °F | |