- 熔体流动速率 [g/10min]: 23.0
- 密度 [g/cm3]: 0.948
- 拉伸强度 [MPa]: 19.0
- 弯曲强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.827
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | |
| Viscosity | 54000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 54000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 116000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 116000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 182000 cP @Shear Rate 300 1/s, Temperature 190 °C | 182000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 23 g/10 min @Load 2.16 kg | 23 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8.5. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | |
| Elongation at Break | 620 % | 620 % | |
| Modulus of Elasticity | 0.552 GPa | 80.1 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.827 GPa | 120 ksi | |
| Izod Impact Resistance | 3.74 J/cm² | 17.8 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 119 °C | 246 °F | |