- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.96
- 拉伸强度 [MPa]: 22.1
- 弯曲强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 1.21
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | |
| Viscosity | 48000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 48000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 73000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 73000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 105000 cP @Shear Rate 300 1/s, Temperature 190 °C | 105000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 30 g/10 min @Load 2.16 kg | 30 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8.5. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | |
| Tensile Strength, Yield | 22.1 MPa | 3210 psi | |
| Elongation at Break | 400 % | 400 % | |
| Modulus of Elasticity | 0.759 GPa | 110 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 1.21 GPa | 175 ksi | |
| Izod Impact Resistance | 3.20 J/cm² | 15.2 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 125 °C | 257 °F | |