- 熔体流动速率 [g/10min]: 0.38
- 密度 [g/cm3]: 0.946
- 拉伸强度 [MPa]: 20.0
- 弯曲模量 [MPa]: 0.565
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | >= 1000 hour | >= 1000 hour | F50, condition B; ASTM D1693 |
| Melt Flow | 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.38 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 0.565 GPa | 81.9 ksi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | insulation resistance |
| Dielectric Constant | 2.34 | 2.34 | ASTM 1531 |
| Dissipation Factor | 0.00010 | 0.00010 | ASTM 1531 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 264 °F | ASTM D3417 |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 230 °C | 410 - 446 °F | |