- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.962
- 拉伸强度 [MPa]: 31.7
- 弯曲模量 [MPa]: 1.55
- 热变形温度 [℃]: 81.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | ASTM D792 |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 69 | 69 | ASTM D2240 |
| Tensile Strength, Yield | 31.7 MPa | 4600 psi | ASTM D638 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Flexural Modulus | 1.55 GPa | 225 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 81.7 °C | 179 °F | Unannealed (0.250 in); ASTM D648 |
| Vicat Softening Point | 129 °C | 264 °F | Rate A, Loading 1 (10 N); ASTM D1525 |