- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.955
- 缺口冲击强度: 2.4
- 拉伸强度 [MPa]: 27.6
- 弯曲模量 [MPa]: 1.38
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ASTM D792 |
| Melt Flow | 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.35 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Flexural Modulus | 1.38 GPa | 200 ksi | ASTM D790 |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in | 73°F, 0.125 in; ASTM D256 |