- 熔体流动速率 [g/10min]: 6.6
- 拉伸强度 [MPa]: 28.3
- 弯曲模量 [MPa]: 1.25
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.953 g/cc | 0.953 g/cc | ASTM D792 |
| Melt Flow | 6.6 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.6 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 22.4 MPa | 3250 psi | ASTM D638 |
| Tensile Strength, Yield | 28.3 MPa | 4110 psi | ASTM D638 |
| Elongation at Break | 7.3 % | 7.3 % | ASTM D638 |
| Flexural Modulus | 1.25 GPa | 181 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 127 °C | 261 °F | Rate A (50°C/h), Loading 1 (10 N); ASTM D1525 |