- 熔体流动速率 [g/10min]: 0.34
- 密度 [g/cm3]: 0.944
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.944 g/cc | 0.0341 lb/in³ | ASTM D792 |
| Water Vapor Transmission | 2.90 g/m²/day | 0.187 g/100 in²/day | ASTM F1249 |
| Thickness | 50.8 microns | 2.00 mil | Blown Film; 2.5:1 BUR; 60 mil die gap |
| Melt Flow | 0.34 g/10 min | 0.34 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 22.1 MPa | 3200 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 27.6 MPa | 4000 psi | ASTM D882 |
| Film Elongation at Break, MD | 590 % | 590 % | ASTM D882 |
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 |
| Secant Modulus, MD | 0.679 GPa | 98.5 ksi | ASTM E111 |
| Secant Modulus, TD | 0.910 GPa | 132 ksi | ASTM E111 |
| Elmendorf Tear Strength MD | 49 g | 49 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1100 g | 1100 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 0.965 g/micron | 24.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 21.7 g/micron | 550 g/mil | ASTM D1922 |
| Film Tensile Strength at Break, MD | 51.4 MPa | 7450 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 46.2 MPa | 6700 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | <= 127.2 °C | <= 261.0 °F | DSC; Lyondell Test |
| Vicat Softening Point | 124.3 °C | 255.7 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 232 °C | 410 - 450 °F | |