- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.958
- 拉伸强度 [MPa]: 29.6
- 弯曲模量 [MPa]: 1.24
- 热变形温度 [℃]: 76.0
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | 80 hour | 80 hour | F50; ASTM D1693 |
| Melt Flow | 0.35 g/10 min | 0.35 g/10 min | ASTM D1238 |
| High Load Melt Index | 35 g/10 min | 35 g/10 min | High load, I-20; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 29.6 MPa | 4300 psi | ASTM D638 |
| Elongation at Break | >= 700 % | >= 700 % | ASTM D638 |
| Flexural Modulus | 1.24 GPa | 180 ksi | 1% Secant; ASTM D790 |
| Tensile Impact Strength | 193 kJ/m² | 92.0 ft-lb/in² | ASTM D1822,S |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Vicat Softening Point | 128 °C | 262 °F | ASTM D1525 |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |