- 熔体流动速率 [g/10min]: 0.075
- 密度 [g/cm3]: 0.949
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| Thickness | 12.7 microns | 0.500 mil | 4:1 BUR; Neck Height = 8 Die Diameters |
| Melt Flow | 0.075 g/10 min | 0.075 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 26.9 MPa | 3900 psi | ASTM D882 |
| Film Elongation at Break, MD | 380 % | 380 % | ASTM D882 |
| Film Elongation at Break, TD | 420 % | 420 % | ASTM D882 |
| Dart Drop, Total Energy | 2.71 J | 2.00 ft-lb | ASTM D3420 |
| Elmendorf Tear Strength MD | 11 g | 11 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 50 g | 50 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 57.9 MPa | 8400 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 46.9 MPa | 6800 psi | ASTM D882 |
| 1% Secant Modulus, MD | 1070 MPa | 155000 psi | ASTM D822 |
| 1% Secant Modulus, TD | 1050 MPa | 152000 psi | ASTM D822 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 210 °C | 390 - 410 °F | Typical Extruder |