- 熔体流动速率 [g/10min]: 0.45
- 密度 [g/cm3]: 0.958
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | 2 - 2.5 BUR; Frost line 24 inch |
| Melt Flow | 0.45 g/10 min | 0.45 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 26.2 MPa | 3800 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 26.9 MPa | 3900 psi | ASTM D882 |
| Film Elongation at Break, MD | 750 % | 750 % | ASTM D882 |
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 |
| Elmendorf Tear Strength MD | 15 g | 15 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 30 g | 30 g | ASTM D1922 |
| 1% Secant Modulus, MD | 827 MPa | 120000 psi | ASTM D822 |
| 1% Secant Modulus, TD | 965 MPa | 140000 psi | ASTM D822 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 216 °C | 390 - 421 °F | Typical Extrusion |