- 熔体流动速率 [g/10min]: 10.0
- 密度 [g/cm3]: 0.945
- 缺口冲击强度: 0.694
- 拉伸强度 [MPa]: 21.39
- 弯曲模量 [MPa]: 0.7046
- 热变形温度 [℃]: 58.7
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D4883 |
| Environmental Stress Crack Resistance | 11 hour | 11 hour | Cond. B, 10%; ASTM D1693 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 21.39 MPa | 3103 psi | at 500 mm; ASTM D638 |
| Elongation at Break | 69 % | 69 % | at 500 mm; ASTM D638 |
| Flexural Modulus | 0.7046 GPa | 102.2 ksi | 1% Secant; ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Temperature -40.0 °C | 1.30 ft-lb/in @Temperature -40.0 °F | ASTM D256 |
| Tensile Impact Strength | 208 kJ/m² | 99.2 ft-lb/in² | -40°C; ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 265 °F | ASTM D3418 |
| Crystallization Temperature | 113 °C | 235 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 58.7 °C | 138 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.6 °C | 99.7 °F | ASTM D648 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |