- 熔体流动速率 [g/10min]: 0.6
- 密度 [g/cm3]: 0.952
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.60 g/10 min @Load 4.76 lb, Temperature 374 °F | ExxonMobil Method | ||
| High Load Melt Index | 10 g/10 min @Load 21.6 kg, Temperature 190 °C | 10 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 37.9 MPa | 5500 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 33.1 MPa | 4800 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 270 % | 270 % | ASTM D882 | ||
| Film Elongation at Break, TD | 380 % | 380 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 7.0 g | 7.0 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 30 g | 30 g | ASTM D1922 | ||
| Dart Drop | 23.6 g/micron | 600 g/mil | ASTM D1709 | ||
| Dart drop Test | 300 g | 0.662 lb | ASTM D1709A | ||
| Film Tensile Strength at Break, MD | 82.7 MPa | 12000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 68.9 MPa | 10000 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 1030 MPa | 150000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 1100 MPa | 160000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 131 °C | 267 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||