- 熔体流动速率 [g/10min]: 0.73
- 密度 [g/cm3]: 0.963
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.963 g/cc | 0.0348 lb/in³ | ASTM D4883 | ||
| Water Vapor Transmission | 11.6 g/m²/day | 0.747 g/100 in²/day | ASTM E969 | ||
| Oxygen Transmission Rate | 5580 cc/m²/day | 359 cc/100 in²/day | ASTM D1434 | ||
| Melt Flow | 0.73 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.73 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| 11 g/10 min @Load 10.0 kg, Temperature 190 °C | 11 g/10 min @Load 22.0 lb, Temperature 374 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 38.6 MPa | 5600 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 34.5 MPa | 5000 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 900 % | 900 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 9.0 % | 9.0 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 0.472 g/micron | 12.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 9.84 g/micron | 250 g/mil | ASTM D1922 | ||
| Dart drop Test | 35.0 g | 0.0772 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 37.2 MPa | 5400 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 30.3 MPa | 4400 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 1030 MPa | 150000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 1140 MPa | 165000 psi | ASTM D882 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.