- 熔体流动速率 [g/10min]: 0.45
- 密度 [g/cm3]: 0.958
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.45 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| High Load Melt Index | 30 g/10 min @Load 21.6 kg, Temperature 190 °C | 30 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 34.5 MPa | 5000 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 13.1 MPa | 1900 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 420 % | 420 % | ASTM D882 | ||
| Film Elongation at Break, TD | 4.0 % | 4.0 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 0.354 g/micron | 9.00 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 30.7 g/micron | 780 g/mil | ASTM D1922 | ||
| Dart Drop | >= 1.57 g/micron | >= 40.0 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 82.7 MPa | 12000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 36.5 MPa | 5300 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 1100 MPa | 160000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 1590 MPa | 230000 psi | ASTM D882 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||