- 熔体流动速率 [g/10min]: 0.46
- 密度 [g/cm3]: 0.957
- 拉伸强度 [MPa]: 30.3
- 弯曲模量 [MPa]: 1.45
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.957 g/cc | 0.0346 lb/in³ | ASTM D4883 | ||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | 100% Igepal; ASTM D1693 | ||
| Melt Flow | 0.46 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.46 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 | ||
| Tensile Strength, Yield | 30.3 MPa | 4400 psi | ASTM D638 | ||
| Elongation at Break | 1100 % | 1100 % | ASTM D638 | ||
| Flexural Modulus | 1.45 GPa | 210 ksi | 1% Secant; ASTM D790 | ||
| Tensile Impact Strength | 252 kJ/m² | 120 ft-lb/in² | ASTM D1822 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||