- 熔体流动速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.953
- 拉伸强度 [MPa]: 28.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in³ | ASTM D4883 | ||
| Melt Flow | 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.25 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| High Load Melt Index | 26 g/10 min @Load 21.6 kg, Temperature 190 °C | 26 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 | ||
| 2% Secant Modulus | 1.24 GPa | 180 ksi | Flexural; ASTM D790 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 177 °C | 350 °F | |||
| Descriptive Properties | |||||
| Notched Constant Ligament Stress | >24 hrs | ASTM F2136 | |||