ExxonMobil Pax-Plus™ 3201 Blown Film Resin

ExxonMobil Pax-Plus™ 3201 Blown Film Resin 物性表: ExxonMobil Pax-Plus™ 3201 Blown Film Resin物性表及特性介绍,ExxonMobil Pax-Plus™ 3201 Blown Film Resin注塑参数详情,如需ExxonMobil Pax-Plus™ 3201 Blown Film Resin下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 0.2
  • 密度 [g/cm3]: 0.936
 
Physical PropertiesMetricEnglishComments
Density 0.936 g/cc0.0338 lb/in³ExxonMobil Method
Thickness 50.8 microns2.00 mil
Melt Flow  0.20 g/10 min
@Load 2.16 kg,
Temperature 190 °C
0.20 g/10 min
@Load 4.76 lb,
Temperature 374 °F
ExxonMobil Method
 4.0 g/10 min
@Load 10.0 kg,
Temperature 190 °C
4.0 g/10 min
@Load 22.0 lb,
Temperature 374 °F
ExxonMobil Method
 
Mechanical PropertiesMetricEnglishComments
Film Tensile Strength at Yield, MD 11.6 MPa1680 psiat 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 12.1 MPa1750 psiat 2% offset; ASTM D882
Film Elongation at Break, MD 700 %700 %ASTM D882
Film Elongation at Break, TD 900 %900 %ASTM D882
Elmendorf Tear Strength MD 70 g70 gASTM D1922
Elmendorf Tear Strength TD 770 g770 gASTM D1922
Elmendorf Tear Strength, MD 1.38 g/micron35.0 g/milASTM D1922
Elmendorf Tear Strength, TD 15.2 g/micron385 g/milASTM D1922
Dart Drop 6.30 g/micron160 g/milASTM D1709
Dart drop Test 320 g0.706 lbASTM D1709
Film Tensile Strength at Break, MD 26.8 MPa3880 psiASTM D882
Film Tensile Strength at Break, TD 23.1 MPa3350 psiASTM D882
1% Secant Modulus, MD 325 MPa47100 psiASTM D882
1% Secant Modulus, TD 387 MPa56200 psiASTM D882
 
Thermal PropertiesMetricEnglishComments
Melting Point 130 °C266 °FPeak Melting Temperature; ExxonMobil Method
Vicat Softening Point 105 °C221 °FExxonMobil Method
 
Descriptive Properties
FeaturesThermal Stabilizer

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-42541.html

免责声明: 本文 ExxonMobil Pax-Plus™ 3201 Blown Film Resin 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4