- 拉伸强度 [MPa]: 42.1
- 弯曲模量 [MPa]: 2.62
- 热变形温度 [℃]: 99.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 73 | 73 | 15s; ASTM D2240 |
| Tensile Strength at Break | 37.2 MPa | 5400 psi | ASTM D638 |
| Tensile Strength, Yield | 42.1 MPa | 6100 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Modulus | 2.62 GPa | 380 ksi | Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790 |
| Gardner Impact | 22.6 J @Temperature 23.0 °C | 16.7 ft-lb @Temperature 73.4 °F | ASTM D3029 |
| Tensile Impact Strength | 52.5 kJ/m² | 25.0 ft-lb/in² | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 µm/m-°C @Temperature 20.0 °C | 50.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ASTM D648 |