- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.941
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in³ | ExxonMobil Method | ||
| Thickness | 50.8 microns | 2.00 mil | |||
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ExxonMobil Method | ||
| 5.8 g/10 min @Load 10.0 kg, Temperature 190 °C | 5.8 g/10 min @Load 22.0 lb, Temperature 374 °F | ExxonMobil Method | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 14.0 MPa | 2030 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 15.2 MPa | 2200 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 | ||
| Film Elongation at Break, TD | 900 % | 900 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 50 g | 50 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 650 g | 650 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 0.984 g/micron | 25.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 12.8 g/micron | 325 g/mil | ASTM D1922 | ||
| Dart Drop | 4.72 g/micron | 120 g/mil | ASTM D1709 | ||
| Dart drop Test | 240 g | 0.529 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 29.8 MPa | 4320 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 26.6 MPa | 3860 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 399 MPa | 57900 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 484 MPa | 70200 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 131 °C | 267 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Vicat Softening Point | 114 °C | 237 °F | ExxonMobil Method | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||