- 熔体流动速率 [g/10min]: 0.045
- 密度 [g/cm3]: 0.952
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | Exxon Method |
| Thickness | 12.7 microns | 0.500 mil | |
| Melt Flow | 0.045 g/10 min | 0.045 g/10 min | Exxon Method (I2). HLMI (I21) is 8 g/10 min. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 37.0 MPa | 5370 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 34.0 MPa | 4930 psi | ASTM D882 |
| Film Elongation at Break, MD | 290 % | 290 % | ASTM D882 |
| Film Elongation at Break, TD | 420 % | 420 % | ASTM D882 |
| Secant Modulus, MD | 1.237 GPa | 179.4 ksi | ASTM D882 |
| Secant Modulus, TD | 1.312 GPa | 190.3 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.433 g/micron | 11.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.72 g/micron | 120 g/mil | ASTM D1922 |
| Dart Drop | 18.1 g/micron | 460 g/mil | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 93.0 MPa | 13500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 63.0 MPa | 9140 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 264 °F | Exxon Method |