- 密度 [g/cm3]: 0.95
- 缺口冲击强度: 5.34
- 拉伸强度 [MPa]: 26.2
- 弯曲模量 [MPa]: 1.210
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D 792 |
| Environmental Stress Crack Resistance | >= 600 hour | >= 600 hour | ASTM D1693 cond. B 100% lgepal |
| High Load Melt Index | 9.0 g/10 min @Load 21.6 kg | 9.0 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 26.2 MPa | >= 3800 psi | ASTM D 638 type IV |
| Elongation at Break | 600 % | 600 % | ASTM D 638, type IV |
| Flexural Modulus | 1.210 GPa | 175.5 ksi | ASTM D 790 |
| Izod Impact, Notched | 5.34 J/cm @Thickness 3.17 mm | 10.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 180 µm/m-°C @Temperature 20.0 °C | 100 µin/in-°F @Temperature 68.0 °F | ASTM D 696 |
| Melting Point | 127 °C | 260 °F | ASTM D3417 |