- 熔体流动速率 [g/10min]: 0.27
- 密度 [g/cm3]: 0.959
- 拉伸强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 1.55
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.959 g/cc | 0.0346 lb/in³ | ISO 1183 |
| Environmental Stress Crack Resistance | >= 200 hour | >= 200 hour | ASTM D1693-70 |
| Melt Flow | 0.27 g/10 min @Load 2.16 kg | 0.27 g/10 min @Load 4.76 lb | ISO 1133 |
| High Load Melt Index | 26 g/10 min @Load 21.6 kg | 26 g/10 min @Load 47.6 lb | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ISO 527 |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ISO 527 |
| Elongation at Break | >= 700 % | >= 700 % | ISO 527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO 527 |
| Flexural Modulus | 1.55 GPa | 225 ksi | ISO 178 |