- 密度 [g/cm3]: 0.9495
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 1.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9495 g/cc | 0.03430 lb/in³ | ISO 1183 |
| Environmental Stress Crack Resistance | >= 360 hour | >= 360 hour | ASTM D1693 cond. B 100% lgepal |
| Thermal Stress Crack Resistance | >= 250 hour | >= 250 hour | ASTM D 1693 |
| High Load Melt Index | 8.0 g/10 min @Load 21.6 kg | 8.0 g/10 min @Load 47.6 lb | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527 |
| Elongation at Yield | 11 % | 11 % | ISO 527 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ISO 178 |
| Impact Test | 20.0 J | 14.8 ft-lb | Multiaxial, @ ULT, deflection = 14 mm; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 127 °C | 261 °F | ASTM D3417 |