- 熔体流动速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.948
- 拉伸强度 [MPa]: 18.0
- 弯曲模量 [MPa]: 0.800
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ISO 1183 |
| Viscosity | 1.30e+6 cP @Shear Rate 100 1/s, Temperature 190 °C | 1.30e+6 cP @Shear Rate 100 1/s, Temperature 374 °F | ATOFINA research test |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | ASTM D1693 cond. B |
| Oxidative Induction Time (OIT) | >= 30 min | >= 30 min | EN 728 |
| Carbon Black Loading | 2.0 - 2.5 % | 2.0 - 2.5 % | ISO 6964 |
| Melt Flow | 0.20 g/10 min @Load 2.16 kg | 0.20 g/10 min @Load 4.76 lb | ISO 1133 |
| 0.92 g/10 min @Load 5.00 kg | 0.92 g/10 min @Load 11.0 lb | ISO 1133 | |
| High Load Melt Index | 18 g/10 min @Load 21.6 kg | 18 g/10 min @Load 47.6 lb | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | DIN 53505 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527 |
| Elongation at Break | >= 700 % | >= 700 % | ISO 527 |
| Elongation at Yield | 9.0 % | 9.0 % | ISO 527 |
| Modulus of Elasticity | 0.700 GPa | 102 ksi | ISO 178 |
| Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D 790 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 93 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | IEC 93 |
| Dielectric Constant | 2.35 @Frequency 1000 Hz | 2.35 @Frequency 1000 Hz | IEC 250 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | IEC 243 |
| Dissipation Factor | 0.00020 @Frequency 1000 Hz | 0.00020 @Frequency 1000 Hz | IEC 250 |
| 0.00030 @Frequency 1e+6 Hz | 0.00030 @Frequency 1e+6 Hz | IEC 250 | |
| Thermal Properties | Metric | English | Comments |
| Heat of Fusion | 152 J/g | 65.4 BTU/lb | DSC |
| CTE, linear | 120 µm/m-°C @Temperature 20.0 °C | 66.7 µin/in-°F @Temperature 68.0 °F | |
| Specific Heat Capacity | 2.00 J/g-°C | 0.478 BTU/lb-°F | DSC |
| 2.60 J/g-°C @Temperature 150 °C | 0.621 BTU/lb-°F @Temperature 302 °F | DSC | |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | DIN 52612 |
| 0.200 W/m-K @Temperature 150 °C | 1.39 BTU-in/hr-ft²-°F @Temperature 302 °F | DIN 52612 | |
| Melting Point | 125 - 129 °C | 257 - 264 °F | crystalline; DSC |
| Vicat Softening Point | 125 °C | 257 °F | ISO 306 |
| Brittleness Temperature | -100 °C | -148 °F | ASTM D 746 |