- 熔体流动速率 [g/10min]: 0.08
- 密度 [g/cm3]: 0.945
- 缺口冲击强度: 5.87
- 拉伸强度 [MPa]: 22.8
- 弯曲模量 [MPa]: 0.862
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D 792 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | No failures; ASTM D1693 cond. C 100% lgepal |
| Melt Flow | 0.080 g/10 min @Load 2.16 kg | 0.080 g/10 min @Load 4.76 lb | ASTM D 1238 |
| 0.34 g/10 min @Load 5.00 kg | 0.34 g/10 min @Load 11.0 lb | ASTM D 1238 | |
| High Load Melt Index | 7.0 g/10 min @Load 21.6 kg | 7.0 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| PENT | >= 100 hour | >= 100 hour | ASTM F 1473 |
| Hardness, Shore D | 63 | 63 | ASTM D 2240 |
| Tensile Strength, Yield | >= 22.8 MPa | >= 3300 psi | ASTM D 638 type IV |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D 638 type IV |
| Flexural Modulus | 0.862 GPa | 125 ksi | ASTM D 790 |
| Izod Impact, Notched | 5.87 J/cm @Thickness 3.17 mm | 11.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Hydrostatic Design Basis | 11.0 MPa | 1600 psi | Room Temperature; ASTM D 2837 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 258 °F | ASTM D3417 |