- 熔体流动速率 [g/10min]: 0.28
- 密度 [g/cm3]: 0.937
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in³ | ASTM D 792 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | ASTM D1693 cond. B 100% lgepal |
| Melt Flow | 0.28 g/10 min @Load 2.16 kg | 0.28 g/10 min @Load 4.76 lb | ASTM D 1238 |
| High Load Melt Index | 20 g/10 min @Load 21.6 kg | 20 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | >= 21.4 MPa | >= 3100 psi | ASTM D 882 A |
| Film Tensile Strength at Yield, TD | >= 21.4 MPa | >= 3100 psi | ASTM D 882 A |
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D 882 A |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D 882 A |
| Elmendorf Tear Strength MD | 50 g | 50 g | ASTM D 1922 |
| Elmendorf Tear Strength TD | 500 g | 500 g | ASTM D 1922 |
| Dart drop Test | 130 g | 0.287 lb | ASTM D 1709 A |
| Film Tensile Strength at Break, MD | 42.1 MPa | 6100 psi | ASTM D 882A |
| Film Tensile Strength at Break, TD | 42.1 MPa | 6100 psi | ASTM D 882A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | ASTM D3417 |