- 密度 [g/cm3]: 0.948
- 缺口冲击强度: 5.34
- 拉伸强度 [MPa]: 22.8
- 弯曲模量 [MPa]: 0.862
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ASTM D 792 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | ASTM D1693 cond. C 100% lgepal |
| High Load Melt Index | 10 g/10 min @Load 21.6 kg | 10 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D 2240 |
| Tensile Strength, Yield | >= 22.8 MPa | >= 3300 psi | ASTM D 638 type IV |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D 638 type IV |
| Flexural Modulus | 0.862 GPa | 125 ksi | ASTM D 790 |
| Izod Impact, Notched | 5.34 J/cm @Thickness 3.17 mm | 10.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 180 µm/m-°C @Temperature 20.0 °C | 100 µin/in-°F @Temperature 68.0 °F | ASTM D 696 |
| Melting Point | 129 °C | 264 °F | ASTM D3417 |