- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 1.25
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ISO 1183 |
| Viscosity | 270000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 270000 cP @Shear Rate 1000 1/s, Temperature 374 °F | ATOFINA research test |
| 2.10e+6 cP @Shear Rate 100 1/s, Temperature 190 °C | 2.10e+6 cP @Shear Rate 100 1/s, Temperature 374 °F | ATOFINA research test | |
| Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
| >= 20 min | >= 20 min | 210°C; EN 728 | |
| Melt Flow | 0.30 g/10 min @Load 5.00 kg | 0.30 g/10 min @Load 11.0 lb | ISO 1133 |
| High Load Melt Index | 8.0 g/10 min @Load 21.6 kg | 8.0 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO 527 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | |
| Elongation at Break | >= 700 % | >= 700 % | ISO 527 |
| Elongation at Yield | 9.0 % | 9.0 % | ISO 527 |
| Flexural Modulus | 1.25 GPa | 181 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 2.00 J/g-°C | 0.478 BTU/lb-°F | DSC |
| 2.60 J/g-°C @Temperature 150 °C | 0.621 BTU/lb-°F @Temperature 302 °F | DSC | |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | DIN 52612 |
| 0.200 W/m-K @Temperature 150 °C | 1.39 BTU-in/hr-ft²-°F @Temperature 302 °F | DIN 52612 | |
| Melting Point | 130 - 132 °C | 266 - 270 °F | crystalline; DSC |