- 密度 [g/cm3]: 0.949
- 缺口冲击强度: 4.27
- 拉伸强度 [MPa]: 24.1
- 弯曲模量 [MPa]: 1.03
- 热变形温度 [℃]: 77.8
- 脆化温度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ISO 1183 |
| High Load Melt Index | 7.5 g/10 min @Load 21.6 kg | 7.5 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| PENT | >= 3000 hour | >= 3000 hour | ASTM F 1473 |
| Tensile Strength, Yield | >= 24.1 MPa | >= 3500 psi | ASTM D 638 type IV |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D 638 type IV |
| Flexural Modulus | 1.03 GPa | 150 ksi | ASTM D 790 |
| Izod Impact, Notched | 4.27 J/cm @Thickness 3.17 mm | 8.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Hydrostatic Design Basis | 11.0 MPa | 1600 psi | Room Temperature; ASTM D 2837 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 180 µm/m-°C @Temperature 20.0 °C | 100 µin/in-°F @Temperature 68.0 °F | ASTM D 696 |
| Melting Point | 131 °C | 268 °F | ASTM D3417 |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.8 °C | 172 °F | ASTM D 648 |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D 1525 |
| Brittleness Temperature | -118 °C | -180 °F | ASTM D 746 |