- 拉伸强度 [MPa]: 17.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.940 g/cc | 0.940 g/cc | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 38.0 MPa | 5510 psi | ISO 2039 | ||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO 527 | ||
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527 | ||
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527 | ||
| Modulus of Elasticity | 0.800 GPa | 116 ksi | ISO 527 | ||
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 179 | ||
| Coefficient of Friction | 0.18 @Temperature 60.0 °C | 0.18 @Temperature 140 °F | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+6 ohm-cm | >= 1.00e+6 ohm-cm | VDE 0303 | ||
| Surface Resistivity per Square | 1.00e+7 ohm | 1.00e+7 ohm | VDE 0303 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.400 W/m-K @Temperature 20.0 °C | 2.78 BTU-in/hr-ft²-°F @Temperature 68.0 °F | DIN 52612 | ||
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |||
| Vicat Softening Point | 76.0 °C | 169 °F | VST/B/50; ISO 306 | ||
| Minimum Service Temperature, Air | -150 °C | -238 °F | |||
| Flammability, UL94 | HB | HB | |||
| Descriptive Properties | |||||
| Acid Resistance | Yes | ||||
| Aromatic Resistance | Limited | ||||
| Bondability | No | ||||
| CKW Resistance | No | ||||
| Hydrocarbonate Resistance | Yes | ||||
| Hydroxide Resistance | Yes | ||||
| Ketone Resistance | Yes | ||||
| Resistance to Hot Water | No | ||||
| UV Stabilization | Limited | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.