- 熔体流动速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.94
- 拉伸强度 [MPa]: 19.0
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | Base Resin; ISO 1183 | ||
| 0.951 g/cc | 0.0344 lb/in³ | Compound; ISO 1183 | |||
| ESCR 10% Igepal® | >= 5000 hour | >= 5000 hour | ASTM D1693-A | ||
| Carbon Black Loading | >= 2.0 % | >= 2.0 % | ASTM D1603 | ||
| Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.20 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 | ||
| 0.85 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.85 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 19.00 MPa | 2755 psi | At 50 mm/min; ISO 527-2 | ||
| Elongation at Break | 600 % | 600 % | ISO 527-2 | ||
| Elongation at Yield | 10 % | 10 % | ISO 527-2 | ||
| Tensile Modulus | 0.800 GPa | 116 ksi | At 1 mm/min; ISO 527-2 | ||
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Front Barrel Temperature | 180 - 210 °C | 356 - 410 °F | |||
| Die Temperature | 200 - 210 °C | 392 - 410 °F | |||
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | |||
| Head Temperature | 200 - 210 °C | 392 - 410 °F | |||
| Descriptive Properties | |||||
| Resistance to Rapid Crack Propagation, BAR | 7 | ISO 13477, Pc at 0°C, S4 / pipe size 250 mm SDR 11 | |||